PHYSICAL
PROPERTIES - CHOCKFAST® ORANGE
|
||
| COEFFICIENT
OF LINEAR THERMAL EXPANSION: Temperature Range 0° to 60°C (32° to 140°F) |
30.8
x 10-6/C° (17.1 x 10-6/F°) |
ASTM D-696 |
| COMPRESSIVE MODULUS OF ELASTICITY: | 37482
kg/cm2 (533,000 psi) |
ASTM D-695 |
| COMPRESSIVE STRENGTH: | 1336
kg/cm2 (19,000 psi) |
ASTM
D-695 (Modified) |
| COVERAGE: | 1966
cc per 3.4 kg (120 cu.in./7.5 lbs.) 4261 cc per 6.8 kg (260 cu.in./15 lbs.) |
|
| CURE TIME: | 48
hrs. 15°C (60°F) 36 hrs. 18°C (65°F) 24 hrs. 21°C (70°F) 18 hrs. 26°C (80°F) |
|
| HARDNESS - BARCOL: | 40-44
fully cured 35 minimum |
ASTM D-2583 |
| FIRE RESISTANCE: | Self-extinguishing |
ASTM D-635 |
IZOD IMPACT STRENGTH: |
0.27
Newton m/cm 6 in.lbs./in. (greater than concrete) |
ASTM D-256 |
| LINEAR SHRINKAGE: | 0.0002
mm/mm (0.0002 in/in) |
ASTM D-2566 |
| POT LIFE: | 30 min. @ 21°C (70°F) | |
| SHEAR STRENGTH: | 380
kg/cm2 (5,400 psi) |
FED-STD-406 (Method 1041) |
| SHELF LIFE: | More than 18 months | |
| SHOCK RESISTANCE: | Pass
MIL-S-901C (Navy) High Impact Shock Test, Grade A, Type A, Class 1 |
|
| SPECIFIC GRAVITY: | 1.58 | |
| TENSILE STRENGTH: | 349
kg/cm2 (4,970 psi) |
ASTM D-638 |
| THERMAL SHOCK: | Pass
-18°C to 100°C (0°F to 212°F) |
ASTM D-746 |
| VIBRATION: | MIL-STD-167 | |